Encapsulated polymerization initiators, polymerization systems and methods using the same

ABSTRACT

An encapsulated initiator particle includes one or more polymerization initiators encapsulated by a cured composition. The cured composition includes one or more 1,1-disubstituted alkene compounds. Polymerizable systems can include one or more encapsulated initiator particles and a polymerizable composition. The polymerizable composition can include one or more 1,1-disubstituted alkene compounds. Methods for forming an encapsulated initiator particle are also described herein.

TECHNICAL FIELD

The present disclosure generally relates to polymerizable systems containing encapsulated initiator particles or materials. The polymerizable systems can be useful as one-part adhesive compositions.

BACKGROUND

Polymerizable compositions are useful components in a number of applications and products and can be used, for example, as an adhesive, a coating, a sealant, a molding, a film, or as a composite binder. Known polymerizable compositions, however, have suffered from a number of significant drawbacks that have limited their potential applications and uses. For example, addition-type polymer systems have required relatively large quantities of polymerization initiators, extensive time requirements, and intense mixing to polymerize which have limited their use to certain applications. Other known polymerizable compositions suffer from other issues that preclude widespread utility. For example, cyanoacrylate compositions suffer from short shelf-lives and difficulty in application due to inactive substrate surfaces. It would therefore be advantageous to provide a polymerizable system that exhibits improved properties including on-demand polymerization without the need for additional ex situ curing agents, superior ease-of-use, long-term shelf stability, and excellent mechanical properties.

SUMMARY

According to one embodiment, an encapsulated initiator particle includes an initiator matrix. The initiator matrix includes a first cured composition formed of one or more 1,1-disubstituted alkene compounds and one or more polymerization initiators substantially encapsulated by the first cured composition

According to another embodiment, a method of forming an encapsulated initiator particle includes the steps of dispersing one or more polymerization initiators in a medium, adding a first polymerizable composition to the medium to form an initiator matrix, terminating residual polymerization of the first polymerizable composition with an anionic polymerization terminator, and adding a second polymerizable composition to the medium to form a shell layer surrounding the initiator matrix. The first polymerizable composition includes one or more 1,1-disubstituted alkene compounds and is polymerizable upon contact with said polymerization initiators. The second polymerizable composition includes one or more 1,1-disubstituted alkene compounds.

According to one embodiment, a mononuclear encapsulated initiator microcapsule includes a shell layer and a polymerization initiator. The shell layer includes a cured composition. The cured composition includes one or more 1,1-disubstituted alkene compounds. The polymerization initiator is encapsulated by the cured composition.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 pictorially depicts different types of encapsulated initiator articles.

FIG. 2 pictorially depicts a matrix encapsulation of polymerization initiators according to one embodiment.

FIG. 3 pictorially depicts a shell encapsulation of an initiator matrix including polymerization initiators according to one embodiment.

FIG. 4 is a chart depicting the tensile shear strength of example polymerizable systems on various substrates.

FIG. 5 is a chart depicting the tensile strength versus cure time of an example polymerizable system.

DETAILED DESCRIPTION

As will be appreciated, polymerizable systems that can be cured on-demand without a polymerization initiator can be used in many applications where initiator-cured systems that require an external initiator are either unusable or undesirable. Such initiator-cured systems can refer to systems that require an additional component, external to the system, to initiate curing. In contrast, polymerizable systems that can be cured without a polymerization initiator can refer to systems that can undergo polymerization without the introduction, or contact, of any additional components external to the system using instead, for example, encapsulated initiators dispersed in the system.

Certain initiator-cured systems are disadvantageous because they are two-part polymerization systems. Two-part polymerization systems generally refer to polymerization systems that require the addition of at least a second component to the system to initiate polymerization.

Addition-type polymerization systems are examples of a two-part polymerization system. Generally, such systems are disadvantageous as a result of the cost and environmental hazards of the initiator components, the energy and time required to mix the initiator components into the polymerizable composition, the time-sensitive application and use of the mixed system, and the continued presence of the initiator components in the cured composition. For example, addition-type acrylate and methacrylate systems require the discrete addition of a relatively large quantity (e.g., about 2% or more) of various initiator components and catalysts into a polymerizable composition to induce polymerization. In such systems, the relatively large quantity of initiator compounds must be meticulously mixed into the system and remain in the cured composition. These disadvantages are a fundamental consequence of a two-part polymerization system and cannot be alleviated by using techniques such as substrate priming or improved initiators.

Other initiator-cured systems include moisture curing systems, such as cyanoacrylate systems, that can be cured upon contact with water or moisture. Although sometimes classified as one-part systems by industry standards, such moisture-sensitive systems suffer from several consequences as a result of using an external initiator. For example, moisture-sensitive curing systems are difficult to control due to their rapid polymerization upon contact with commonly found surface moisture, which can vary widely in concentration substrate to substrate and with seasonal atmospheric humidity. As such, they are unsuitable for use in certain applications such as those pertaining to various inorganic and/or acidic substrates. Additionally, cyanoacrylates also suffer from fairly limited physical and performance versatility. Attempts to improve cyanoacrylate systems through the addition of primers or additives have increased the complexity of use as well as the expense of such systems.

A polymerizable system that can be cured without the addition of an external polymerization initiator, such as a system that can be cured with pressure or force, can avoid these issues and can be used in a wide range of applications that are unsuitable for initiator-cured polymerization systems. For example, such systems can be readily stored as a usable composition, and can be polymerized without additional components, or the time constraints and mixing required in initiator-cured systems.

A polymerizable system with improved properties, including self-initiated polymerization without the addition of any external curing agent sources, can generally include a polymerizable composition and an encapsulated polymerization initiator dispersed within the polymerizable composition. Advantageously, such polymerizable systems can alleviate many of the problems of known polymerization systems and can be cured by rupturing encapsulated polymerization initiators.

According to certain embodiments, suitable polymerizable compositions and polymerization initiators can be selected from any pair of components that react upon contact with one another to initiate polymerization. However, particularly advantageous polymerizable compositions can be 1,1-disubstituted alkene compounds having two carbonyl groups bonded to the 1 carbon and a hydrocarbyl group bonded to each of the carbonyl groups (“hereinafter 1,1-disubstituted alkene compounds”). In such 1,1-disubstituted alkene compounds, the hydrocarbyl groups can be bonded to the carbonyl groups directly or through an oxygen atom.

According to certain embodiments, suitable hydrocarbyl groups can include at least straight or branched chain alkyl groups, straight or branched chain alkyl alkenyl groups, straight or branched chain alkynyl groups, cycloalkyl groups, alkyl substituted cycloalkyl groups, aryl groups, aralkyl groups, and alkaryl groups. Additionally, suitable hydrocarbyl groups can also contain one or more heteroatoms in the backbone of the hydrocarbyl group.

In certain embodiments, a suitable hydrocarbyl group can also, or alternatively, be substituted with a substituent group. Non-limiting examples of substituent groups can include one or more alkyl, halo, alkoxy, alkylthio, hydroxyl, nitro, cyano, azido, carboxy, acyloxy, and sulfonyl groups. In certain embodiments, substituent groups can be selected from one or more alkyl, halo, alkoxy, alkylthio, and hydroxyl groups. In certain embodiments, substituent groups can be selected from one or more halo, alkyl, and alkoxy groups.

In certain embodiments, suitable hydrocarbyl groups can be C₁₋₂₀ hydrocarbyl groups. For example, the hydrocarbyl group can be an alkyl ether having one or more alkyl ether groups or alkylene oxy groups. Suitable alkyl ether groups can include, without limitation, ethoxy, propoxy, and butoxy groups. In certain embodiments, suitable hydrocarbyl groups can contain about 1 to about 100 alkylene oxy groups; in certain embodiments, about 1 to about 40 alkylene oxy groups; and in certain embodiments, about 1 to about 10 alkylene oxy groups. In certain embodiments, suitable hydrocarbyl groups can contain one or more heteroatoms in the backbone.

Suitable examples of more specific hydrocarbyl groups can include, in certain embodiments, C₁₋₁₅ straight or branched chain alkyl groups, C₁₋₁₅ straight or branched chain alkenyl groups, C₅₋₁₈ cycloalkyl groups, C₆₋₂₄ alkyl substituted cycloalkyl groups, C₄₋₁₈ aryl groups, C₄₋₂₀ aralkyl groups, and C₄₋₂₀ alkaryl groups. In certain embodiments, the hydrocarbyl group can more preferably be C₁₋₈ straight or branched chain alkyl groups, C₅₋₁₂ cycloalkyl groups, C₆₋₁₂ alkyl substituted cycloalkyl groups, C₄₋₁₈ aryl groups, C₄₋₂₀ aralkyl groups, or C₄₋₂₀ alkaryl groups.

As used herein, alkaryl can include an alkyl group bonded to an aryl group. Aralkyl can include an aryl group bonded to an alkyl group. Aralkyl can also include alkylene bridged aryl groups such as diphenyl methyl or propyl groups. As used herein, aryl can include groups containing more than one aromatic ring. Cycloalkyl can include groups containing one or more rings including bridge rings. Alkyl substituted cycloalkyl can include a cycloalkyl group having one or more alkyl groups bonded to the cycloalkyl ring.

In certain embodiments, suitable alkyl groups can include methyl, ethyl, propyl, isopropyl, butyl, tertiary butyl, pentyl, hexyl, and ethyl hexyl. Similarly, examples of suitable cycloalkyl groups can include cyclohexyl and fenchyl groups. Examples of suitable alkyl substituted groups can include menthyl and isobornyl groups.

According to certain embodiments, suitable hydrocarbyl groups can include methyl, ethyl, propyl, isopropyl, butyl, tertiary butyl, ethyl pentyl, hexyl, ethyl hexyl, fenchyl, menthyl, and isobornyl groups.

In certain embodiments, illustrative examples of 1,1-disubstituted alkene compounds can include methylene malonates, methylene β-ketoesters, methylene β-di-ketones, di-alkyl di-substituted vinyls, di-haloalkyl di-substituted vinyls and any monofunctional, difunctional, or multifunctional monomers, oligomers, or polymers thereof. As can be appreciated, one or more of such illustrative examples can be used as a suitable polymerizable composition according to certain embodiments.

Generally, 1,1-disubstituted alkene compounds can have a variety of properties that make them particularly suitable for use in forming a polymerizable composition. For example, 1,1-disubstituted alkene compounds can exhibit water tolerance, can be optically clear in both cured and uncured states, and can have excellent adhesion properties and cure times. Additionally, 1,1-disubstituted alkene compounds can be readily polymerized upon exposure to a mild nucleophilic (or basic) agent without requiring energy-reactive conditions or mixing. For example, 1,1-disubstituted alkene compounds can polymerize at ambient conditions (e.g., at about room temperature and pressure).

In certain embodiments, 1,1-disubstituted alkene compounds can be monofunctional, difunctional, or multifunctional. Monofunctional compounds can refer to monomers that have a single addition polymerizable group. Difunctional compounds can refer to monomers, oligomers, resins, or polymers that contain two addition polymerizable groups. Multifunctional compounds can refer to any monomer, oligomer, resin, or polymer that contains three or more addition polymerizable groups. In contrast to monofunctional compounds, certain difunctional compounds and multifunctional compounds can undergo additional crosslinking, chain extension, or both when exposed to certain suitable polymerization initiators.

An illustrative example of a monofunctional 1,1-disubstituted alkene compound is depicted by general formula I:

wherein each X can independently be O or a direct bond and R₁ and R₂ can be the same or different and can each represent a hydrocarbyl group.

An illustrative example of a multifunctional monomer having more than one methylene group connected by a multivalent hydrocarbyl group can be depicted by general formula II:

wherein each X can independently be O or a direct bond; R₃ and R₅ can be the same or different and can each represent a hydrocarbyl group; R₄ can be a hydrocarbyl group having n+1 valences; and n is an integer of 1 or greater. In certain embodiments, n can be 3 or fewer; and in certain embodiments, n can be 2 or fewer.

According to certain embodiments, specific examples of suitable polymerizable compositions can include methylene malonate compounds having general formula III:

wherein R₆ and R₇ can be the same or different and can each represent a hydrocarbyl group. For example, in certain more specific embodiments, suitable methylene malonate compounds can include one or more of diethyl methylene malonate (“DEMM”), dimethyl methylene malonate (“DMMM” or “D3M”), hexyl methyl methylene malonate (“HMMM”), ethylethoxy ethyl methylene malonate (“EEOEMM”), fenchyl methyl methylene malonate (“FMMM”), dibutyl methylene malonate (“DBMM”), di-n-propyl methylene malonate, di-isopropyl methylene malonate, and dibenzyl methylene malonate. Additionally, in certain embodiments, certain transesterification reaction products formed from the reaction of methylene malonate compounds with acetates, diacetates, alcohols, diols, and polyols can also be used to form a suitable polymerizable composition.

According to certain embodiments, examples of suitable methylene beta ketoesters can be represented by general formula IV:

wherein R₈ and R₉ can be the same or different and can each represent a hydrocarbyl group.

According to certain embodiments, examples of suitable methylene beta diketones can be represented by general formula V:

wherein R₁₀ and R₁₁ can be the same or different and can each represent a hydrocarbyl group.

Additional details and methods of making suitable 1,1-disubstituted alkene compounds as well as other suitable polymerizable compositions are disclosed in U.S. Pat. No. 8,609,885; U.S. Pat. No. 8,884,051; and WO 2014/110388 each of which are hereby incorporated by reference.

According to certain embodiments, a suitable polymerization initiator can generally be selected from any agent that can initiate polymerization substantially upon contact with a selected polymerizable composition. In certain embodiments, it can be advantageous to select polymerization initiators that can induce polymerization under ambient conditions and without requiring external energy from heat or radiation.

In embodiments wherein the polymerizable composition is a 1,1-disubstituted alkene compound, a wide variety of polymerization initiators can be suitable including most nucleophilic initiators capable of initiating anionic polymerization. For example, suitable initiators include alkali metal salts, alkaline earth metal salts, ammonium salts, amine salts, halides (halogen containing salts), metal oxides, and mixtures containing such salts or oxides. Exemplary anions for such salts include anions based on halogens, acetates, benzoates, sulfur, carbonates, silicates and the like. The mixtures containing such salts can be naturally occurring or synthetic. Specific examples of suitable polymerization initiators for 1,1-disubstituted alkene compounds can include glass beads (being an amalgam of various oxides including silicon dioxide, sodium oxide, and calcium oxide), ceramic beads (comprised of various metals, nonmetals, and metalloid materials), clay minerals (including hectorite clay and bentonite clay), and ionic compounds such as sodium silicate, sodium benzoate, and calcium carbonate. Other polymerization initiators can also be suitable including certain plastics (e.g., ABS, acrylic, and polycarbonate plastics) and glass-fiber impregnated plastics. Additional suitable polymerization initiators for such polymerizable compositions are also disclosed in U.S. Patent App. Publication No. 2015/0073110, which is hereby incorporated by reference.

As can be additionally appreciated, in embodiments wherein the polymerizable composition is a 1,1-disubstituted alkene compound, neither water nor atmosphere appreciably initiates polymerization of the 1,1-disubstituted alkene compounds. Such environmental tolerances limit undesirable reactivity of composition prior to curing by deliberate exposure to a polymerization initiator.

According to certain embodiments, a polymerizable initiator can be encapsulated before inclusion in a polymerizable system. Encapsulation of the polymerizable initiator inhibits reactivity of the initiator and can allow for the creation of a polymerizable system that acts as a “one-part” system. As used herein, a “one-part” system can mean that a system can be cured without the addition of any external curing agents. A one-part polymerizable system including encapsulated polymerization initiators can instead cure by rupturing the encapsulated initiator particles to expose the polymerization initiators inside of the encapsulated initiator particles. As used herein, rupturing can mean damage to the encapsulated particle or microcapsule housing the polymerization initiators, thus exposing the polymerization initiator to the surrounding environment. As can be appreciated, rupturing can occur, or can be achieved, in a variety of ways including through mechanical or thermal means such as applied force or thermal shock. However, other methods of rupturing can be further contemplated including the use of ultrasonic vibrations and laser heating.

Generally, any type of encapsulation technique can be used including, for example, encapsulation of a suitable polymerization initiator to produce a mononuclear, polynuclear, or matrix encapsulated polymerization initiators. Each of these three types of encapsulated articles are generally depicted in FIG. 1. A mononuclear polymerization initiator can include a single polymerization initiator encapsulated by a non-reactive shell. A polynuclear polymerization initiator can include several polymerization initiators, each encapsulated by a surrounding shell. An initiator matrix can be formed of polymerization initiators substantially encapsulated into a cured composition (e.g., a binder).

According to certain embodiments, a suitable matrix encapsulated initiator particle can be prepared using a two-phase synthetic scheme. In such embodiments, the synthetic scheme can include a step of forming an initiator matrix of polymerization initiators and a step of encapsulating the initiator matrix with a shell layer.

In certain embodiments, the first step of producing an initiator matrix of polymerization initiators can be performed using a matrix encapsulation process. In an illustrative matrix encapsulation process, an initiator matrix containing polymerization initiators can be formed by dispersing suitable polymerization initiators into a medium and subsequently reacting the polymerization initiators with a desired quantity of a reactive composition as depicted in FIG. 2. The reactive composition can polymerize upon contact with the polymerization initiator and can encapsulate the polymerization initiator to form an initiator matrix including polymerized monomers and polymerization initiators. Any remaining residual polymerization can then be terminated by the addition of an appropriate termination compound or agent. In certain embodiments, polymerization can occur with constant agitation of the medium.

According to certain embodiments, the step of terminating residual polymerization can improve the production and yield of initiator matrices. For example, in certain matrix polymerization processes not including a termination step, only about 50% to about 80% of the polymerization initiators can be encapsulated by the addition of a reactive composition. The addition of a termination step to the same matrix polymerization process, however, can encapsulate about 100% of the polymerization initiators. Additionally, the step of terminating residual polymerization can also prevent agglomeration of multiple matrices together by lowering the reactivity of each of the individual matrices.

In certain embodiments encapsulating a polymerization initiator, the reactive composition can be a 1,1-disubstituted alkene compound such as a methylene malonate compound. As can be appreciated, such 1,1-disubstituted alkene compounds can react upon contact with a polymerization initiator and can polymerize to form initiator matrices. In such embodiments, a suitable termination compound can be any suitable anionic polymerization terminator including, for example, mineral acids such as methanesulfonic acid, sulfuric acid, and phosphoric acid and carboxylic acids such as acetic acid and trifluoroacetic acid. In certain embodiments, a suitable anionic polymerization terminator can be trifluoroacetic acid and can be added until the medium containing the encapsulated matrices is slightly acidic (e.g., at about 6 pH).

According to certain embodiments, the reactive composition can be the same or similar to the polymerizable composition of a polymerizable system. This similarity can confer certain benefits to the system. For example, a polymerizable system can have improved stability after the step of curing the system because the cured composition will be formed only of similarly-classed polymers with good compatibility. Further, the use of 1,1-disubstituted alkene compounds can also be individually advantageous because such compounds can produce encapsulated initiators that can rupture with forces that are particularly amenable to use. For example, encapsulated initiator particles formed with methylene malonate compounds as the matrix binder can rupture when a force of about 0.1 psi or more is applied to the particle in certain embodiments, when about 0.5 psi or more is applied to the particle in certain embodiments, or when about 1 psi or more of force is applied to the particle in certain embodiments. Encapsulated initiator particles that rupture with such amenable forces can also rupture in a polymerizable composition with particularly advantageous forces. For example, such encapsulated initiator particles, when further including a shell layer and when dispersed in a polymerizable composition, can rupture and initiate curing when about 50 psi or less of force is applied to the composition in certain embodiments, when about 30 psi or less of force is applied to the composition in certain embodiments, when about 10 psi or less of force is applied to the composition in certain embodiments, or when about 5 psi or more of force is applied to the composition in certain embodiments.

According to certain embodiments, a reactive composition can also be formed of 1,1-disubstituted alkene compounds that form polymers having different glass transition temperatures (“Tg”). For example, a reactive composition can be formed of 1,1-disubstituted alkene compounds that polymerize to a low temperature Tg polymer or polymerize to an elevated temperature Tg polymer (hereinafter “low Tg 1,1-disubstituted alkene compounds” and “elevated Tg 1,1-disubstituted alkene compounds” respectively). In certain embodiments, it can also be advantageous to form a reactive composition formed of a blend of both low Tg 1,1-disubstituted alkene compounds and elevated Tg 1,1-disubstituted alkene compounds. Reactive compositions including blends of mixed glass transition temperature 1,1-disubstituted alkene compounds can prevent coalescence of the initiator matrices and/or improve the rigidity of the matrix encapsulation.

In embodiments where a reactive composition includes a blend of both low Tg and elevated Tg 1,1-disubstituted alkene compounds, the reactive composition can include various quantities of low Tg and elevated Tg 1,1-disubstituted alkene compounds. For example, in certain embodiments, about 85% to about 99%, by weight, of a reactive composition can be formed of low Tg 1,1-disubstituted alkene compounds such as hexyl methyl methylene malonate. In certain embodiments, about 90% to about 97.5%, by weight, of a reactive composition can be formed of low Tg 1,1-disubstituted alkene compounds. A low Tg 1,1-disubstituted alkene compound can have a Tg of about 0° C. or less according to certain embodiments, or a Tg of about −10° C. or less according to certain embodiments. Examples of suitable low Tg 1,1-disubstituted alkene compounds can include methylmethoxy ethyl methylene malonate (0° C.), ethylethoxy ethyl methylene malonate (−18° C.), hexyl methyl methylene malonate (−34° C.), and dibutyl methylene malonate (−44° C.).

In such reactive composition blends of low Tg and elevated Tg 1,1-disubstituted alkene compounds, at least a portion of the remaining reactive composition can be elevated Tg 1,1-disubstituted alkene compounds. For example, in certain embodiments about 1% to about 15%, by weight, of the reactive composition can be an elevated Tg 1,1-disubstituted alkene compound. In certain embodiments, about 2.5% to about 5%, by weight, of the reactive composition can be an elevated Tg 1,1-disubstituted alkene compound. Elevated Tg 1,1-disubstituted alkene compounds can have a Tg of about room temperature (e.g., about 23° C.) or greater in certain embodiments, a Tg of about 30° C. or greater in certain embodiments, or a Tg of about 50° C. or greater in certain embodiments. Non-limiting examples of suitable elevated Tg 1,1-disubstituted alkene compounds can include diethyl methylene malonate (35° C.), dimethyl methylene malonate (55° C.), phenylpropyl methyl methylene malonate (50-70° C.), menthyl methyl methylene malonate (125-135° C.), and fenchyl methyl methylene malonate (140-190° C.). Certain elevated Tg 1,1-disubstituted compounds can be suitable due to crosslinking with difunctional or multifunctional 1,1-disubstituted alkene compounds. For example, the substitution of a diethyl methylene malonate composition (Tg of 35° C.) with about 10% difunctional pentane or hexane linked ethyl methylene malonate can increase the Tg of the diethyl methylene malonate composition by about 10° C. to reach an elevated Tg of about 45-55° C. and can be used as an elevated Tg 1,1-disubstituted alkene compound.

Matrix encapsulation can occur in a medium by dispersing both a polymerization initiator and a reactive composition into the medium. Appropriate mediums for the matrix encapsulation can be selected based on the reactivity and solubility of both the polymerization initiator and the reactive composition. For example, matrix encapsulation of glass beads or clay with diethyl methylene malonate can occur in a distilled or deionized aqueous medium as neither component is reactive with water. Conversely, matrix encapsulation of a salt such as sodium silicate can necessitate the use of an organic medium such as heptane.

In certain embodiments, the properties of an encapsulated initiator particle or microcapsule can be influenced through various modifications to the initiator, the reactive monomer, or through the addition of other components.

For example, in certain embodiments, the size and shape of a polymerization initiator can be selected based upon the intended use of the polymerizable system. Larger particle sizes can be selected, for example, when the polymerizable system is intended to be used as an adhesive to bond a relatively porous substrate, such as wood or ceramics, because the larger particles can fill in gaps in the porous substrate. Conversely, a relatively small particle size can be selected when the polymerizable system is intended to be used as an adhesive to bond non-porous surfaces such as a smooth metal substrate. These changes reflect that the size and shape of the polymerization initiator can affect the rheological and mechanical properties of the system. Additionally, initiators can also act as reinforcement material in the cured polymerizable systems and thus, the size, shape, and material selected can influence the strength and rigidity of the cured systems. Examples of such reinforcing initiators can include material-based initiators such as glass beads and fibers, ceramic beads, clays, polymeric additives (i.e., thermoplastic elastomers and tougheners), woven materials, and nucleophilic silica. Generally, initiators can be in any suitable shape or form and can be, for example, spherical, non-spherical, irregular, angular, textured, or layered. Suitable polymerization initiators can generally be about 0.1 microns to about 1,000 microns in average granulometry according to certain embodiments; about 50 microns to about 750 microns in average granulometry according to certain embodiments; and about 100 microns to about 500 microns in average granulometry according to certain embodiments. Granulometry can refer to the particle size as determined through any known technique including dynamic light scatting, imaging particle analysis, calibrated sieves or filters, and optical inspection or microscopy.

Alternatively or additionally, the reactive composition can be selected, or modified, to influence several properties including the adhesion strength of the polymerizable system, the elasticity of the system, and the propensity of the encapsulated initiator particles or microcapsules to agglomerate, or coalesce, in a polymerizable system. For example, the rheological properties of a system including encapsulated initiator particles or microcapsules can be influenced by selecting a reactive composition which polymerizes to form polymers with an appropriate glass transition temperature. In certain embodiments, the reactive composition can also be modified by using more than one reactive compound. For example, a blend of an elevated Tg 1,1-disubstituted alkene compound such as, for example, diethyl methylene malonate, with a low Tg 1,1-disubstituted alkene compound such as, for example, hexyl methyl methylene malonate, can be used to prevent undesirable agglomeration, or coalescence, of the encapsulated polymerization initiators in certain polymerizable systems. The glass transition temperature of an encapsulated polymerization initiator can also be influenced by the respective glass transition temperatures of the individual reactive compounds.

According to certain embodiments, the matrix encapsulation step can include further components. For example, in certain embodiments, a suitable plasticizer can be included with a reactive composition. Generally, suitable plasticizers can include plasticizers used to modify the rheological properties of adhesive systems including, for example, straight and branched chain alkyl-phthalates such as diisononyl phthalate, dioctyl phthalate, and dibutyl phthalate, as well as partially hydrogenated terpene, trioctyl phosphate, epoxy plasticizers, toluene-sulfamide, chloroparaffins, adipic acid esters, sebacates such as dimethyl sebacate, castor oil, xylene, 1-methyl-2-pyrrolidione and toluene. Commercial plasticizers such as HB-40 manufactured by Solutia Inc. (St. Louis, Mo.) can also be suitable. The inclusion of a plasticizer can generally influence the robustness and elasticity of the particle or microcapsule. In certain embodiments, about 5% or less of a reactive monomer can be substituted with a plasticizer.

In certain embodiments, the encapsulated initiator particle can still be reactive after the step of matrix encapsulation and/or be relatively tacky. Such issues can be alleviated by a second, shell encapsulation, step. In a shell encapsulation step, a shell can be polymerized around an initiator matrix by adding an additional reactive composition. Initiation of the resulting shell can occur from contact to exposed polymerization initiators on the surface of the initiator particle and, when a termination step is not performed after matrix encapsulation, by contact with active propagating polymers chains from the encapsulated initiator particles. In certain embodiments, the shell encapsulation step can occur in a medium and can occur with agitation. An example shell encapsulation step is generally depicted in FIG. 3.

As can be appreciated, the additional reactive composition can include the same reactive compound used in the matrix encapsulation step or can include a different reactive compound depending on the desired properties of the system. For example, in certain embodiments, diethyl methylene malonate can be used as the reactive compound in both the matrix encapsulation of the one or more initiators and the shell encapsulation of the initiator matrix. However, in other suitable examples, the shell layer reactive compositions can include one or more other 1,1-disubstituted alkene compounds or other compounds. For example, a suitable shell layer can be formed from a blend of diethyl methylene malonate with pentane or hexane linked difunctional monomers. Similarly to certain matrix encapsulation reactive compositions, the additional reactive composition can also, or alternatively, include a blend of 1,1-disubstituted alkene compounds that form polymers having different glass transition temperatures to improve rigidity of the shell layer and to reduce agglomeration or coalescence. In such embodiments, an elevated Tg 1,1-disubstituted alkene compound having, for example, a Tg of about room temperature or greater, or a Tg of about 50° C. or greater can be included in the additional reactive composition.

In certain embodiments, it can also be advantageous for the additional reactive composition to include difunctional or multifunctional compounds. The inclusion of difunctional and/or multifunctional compounds into the shell layer can allow for crosslinking of the cured oligomers or polymers to occur. In certain embodiments including difunctional or multifunctional compounds in the additional reactive composition, about 5% to about 15%, by weight, of the shell can be formed of the difunctional or multifunctional compounds. The resulting crosslinked shells can be stronger, with decreased permeability to the surrounding environment, and less reactive than shells formed from only monofunctional compounds. Additional modifications to the shell encapsulation step can also be performed, including, for example, the inclusion of a plasticizer.

Generally, after formation of a shell layer around the initial matrix, residual polymerization can be terminated by addition of an appropriate anionic polymerization terminator such as a weak acid (e.g., trifluoroacetic acid). The encapsulated initiator particles can then be rinsed and cleaned with deionized water. In certain embodiments, a subsequent rinsing process can be performed with a slightly acidic deionized water wash (e.g., about 6 pH) to passivate the encapsulated initiator particles.

Other techniques can also be used to prepare encapsulated polymerization initiators. For example, in certain embodiments, a matrix encapsulation step can be replaced by an alternative step that encapsulates a polymerization initiator with a non-reactive compound such as a wax compound (e.g., molten polyethylene wax). In certain embodiments, an initiator matrix formed through such alternative methods can subsequently be exposed to a reactive monomer to polymerize a shell layer.

Alternatively, in certain embodiments, the step of shell encapsulation can be replaced by other known encapsulation techniques. For example, shells could be formed around initiator matrices using one or more of a urea formaldehyde resin, a polyvinyl alcohol, a gelatin, an acrylate, or an oligomeric reactive monomer such as oligomeric isocyanate or epoxy functional resins. Other encapsulation techniques are disclosed in U.S. Patent App. Publication No. 2005/0067726, which is hereby incorporated by reference.

Encapsulated polymerization initiators can be non-reactive after encapsulation steps and can be added directly to a polymerizable composition to form a polymerizable system. However, as can be further appreciated, encapsulated polymerization initiators can also be stored separately from any polymerization composition and can then be added to the polymerizable composition at a later point prior to use. Depending upon the properties of the encapsulated polymerization initiators and the polymerizable composition, agglomeration of the encapsulated polymerization initiators can occur. In such situations, the addition of a thixotropic agent or anti-caking agent, such as fumed silica, can allow for proper dispersion of the encapsulated polymerization initiators within the polymerizable composition.

According to certain embodiments, certain polymerizable systems can also include other additional components. For example, one or more dyes, pigments, toughening agents, impact modifiers, rheology modifiers, plasticizing agents, natural or synthetic rubbers, filler agents, reinforcing agents, thickening agents, opacifiers, inhibitors, fluorescence markers, thermal degradation reducers, thermal resistance conferring agents, surfactants, wetting agents, or stabilizers can be included in a polymerizable system. For example, thickening agents and plasticizers such as vinyl chloride terpolymer (comprising vinyl chloride, vinyl acetate, and dicarboxylic acid at various weight percentages) and dimethyl sebacate respectively, can be used to modify the viscosity, elasticity, and robustness of a system. In certain embodiments, such thickening agents and other compounds can be used to increase the viscosity of a polymerizable system from about 1 to 3 cPs to about 30,000 cPs, or more.

According to certain embodiments, stabilizers can be included in a polymerizable system to increase and improve the shelf life and to prevent spontaneous polymerization. Generally, one or more anionic polymerization inhibitors such as liquid phase stabilizers (e.g., methanesulfonic acid (“MSA”)), vapor phase stabilizers (e.g., trifluoroacetic acid (“TFA”)), or free-radical stabilizers (e.g., 4-methoxyphenol or mono methyl ether of hydroquinone (“MeHQ”)) can be used as a stabilizer package as disclosed in U.S. Pat. No. 8,609,885 and U.S. Pat. No. 8,884,051, each incorporated by reference. Additional free radical polymerization inhibitors are disclosed in U.S. Pat. No. 6,458,956 and are hereby incorporated by reference. Anionic polymerization stabilizers are generally electrophilic compounds that scavenge electrons from the composition or growing polymer chain. The use of anionic polymerization stabilizers can terminate additional polymer chain propagation. Generally, only minimal quantities of a stabilizer are needed and, in certain embodiments only about 150 parts-per-million (“ppm”) or less can be included. In certain embodiments, a blend of multiple stabilizers can be included such as, for example, a blend of about 10 ppm MSA and 100 ppm MeHQ.

One-part polymerizable systems including encapsulated polymerization initiators can be used for a variety of applications. For example, in certain embodiments, the polymerizable systems can be used as an adhesive. When used as an adhesive, the polymerizable systems can have excellent properties including a viscosity of about 3,000 cPs to about 5,000 cPs, a set time of about 5 minutes to about 10 minutes on non-porous substrates, and a cure time of about 4 hours. Advantageously, such application times are amenable to both easy positioning and cleanup. Set time, as used herein, is defined as the ability of an adhesive composition to withstand a shear force of 0.2 N/mm² for 10 seconds or more. Cure time, as used herein, can mean that 75% or more of the composition has been polymerized. Once the cure time has been reached, the polymerized composition can exhibit maximum mechanical strength properties.

The one-part polymerizable systems can also have excellent shelf life. For example, such systems can have a shelf life of at least 12 days at 50° C., and/or a shelf life of 20 weeks or more at ambient temperatures. A shelf life of 12 days at 50° C. can indicate a life span under ambient conditions of about six months or more in certain embodiments, and a life span of about one year or more in certain embodiments.

The tensile shear strengths of such polymerizable systems can vary and can be, for example, 1,000 psi or more on steel, 1,100 psi or more on hard maple wood, and 900 psi or more on polycarbonate. Additionally, the polymerizable composition does not bond skin.

In certain embodiments, the polymerizable systems can also be advantageously used as a threadlocking composition. In such embodiments, a polymerizable composition can be applied to a bolt or nut. Tightening of the nut can rupture the encapsulated initiator particles via mechanical shear and expose the polymerization initiators to the polymerizable composition. Such threadlocking compositions can be advantageous because it allows for a one-part application that can be activated when the nut or bolt is tightened, irrespective of substrate composition. In contrast, known two-part polymerizable systems require application of two components to the nut or bolt and must be used immediately after application of the second component. In certain embodiments, the present threadlocking compositions can additionally exhibit stronger break-loose torques than similar, conventionally cured systems. Additionally, certain systems can also exhibit stronger resistance to heat, cold, or dissolution in various liquids and solvents. For example, a steel bolt and zinc-plated nut system treated with a threadlocking composition can have a set time of about 15 minutes to about 30 minutes and can require torque of about 12 Nm to break loose. In a second example, a threadlocking composition can have a set time of about 5 minutes and can require torque of about 29 Nm to break loose after curing of about 24 hours. Additionally, the second example can exhibit resistance to 120° C. heat, −20° C. cold, as well as resistance to gasoline, acetone, and boiling water.

Examples

A variety of encapsulated initiator particles/microcapsules and polymerizable systems are depicted in Table 1. Table 1 includes Examples 1 to 8 and depicts the components of a matrix encapsulation step.

TABLE 1 Example Example Example Example Example Example Example Example Components 1 2 3 4 5 6 7 8 Glass Beads 5 g — — 5 g 5 g 5 g 5 g 5 g Sodium — 5 g — — Silicate Clay — — 5 g — — — — — (Bentone SD-2) H₂O 200 g — 200 g 200 g 200 g 200 g 200 g 200 g Heptane — 200 g — — — — — — DEMM 2.5 g 2.5 g 2.5 g 1.875 g 2.25 g — — 0.25 g DMMM — — — — — — 1.875 g — EEOEMM — — — 0.625 g — — — — HMMM — — — — — 2.44 g 0.625 g — DBMM — — — — — — — 2.25 g TFA 0.02 g 0.02 g 0.02 g 0.02 g 0.02 g 0.02 g 0.02 g 0.02 g Dimethyl — — — — 0.25 g 0.06 g — — Sebacate

The matrix encapsulation depicted in each of Examples 1 to 8 proceeds similarly. Initially, polymeric initiators (glass beads, sodium silicate, or clay) are uniformly dispersed in a medium (H₂O or heptane) by mixing at 1,000 rpm. Subsequently, a reactive composition (DEMM, EEOEMM, or HMMM) is added dropwise to the medium and allowed to polymerize for one hour under continued agitation. Trifluoroacetic acid is then added to terminate any residual polymerization. The initiator matrices are then filtered and rinsed with deionized water. In Examples 5 and 6, a plasticizer (dimethyl sebacate) is added dropwise with the reactive monomer and included as part of the resulting matrix.

Each of Examples 1 to 8 demonstrate good encapsulation qualities. Examples 1 to 3, for example, produce high strength initiator matrices that do not crush (i.e., rupture) under applied pressure of 10 psi to 30 psi. Copolymerization with DEMM and EEOEMM in Example 4 produce elastic initiator matrices that can restore their shapes after deformations. The elastic initiator matrices of Example 4 rupture after application of minimal pressure such as hand pressure. Examples 5 and 6 incorporate a plasticizer. The incorporation of the plasticizer in Examples 5 and 6 reduce robustness and produce initiator matrices that rupture with hand pressure. However, the low glass transition temperature of HMMM in Example 6 allow for initiator matrices that are sufficiently robust for processing despite the plasticizer. Examples 7 and 8 are also suitable.

Table 2 depicts Examples 9 and 10 and illustrates the percentage of glass bead initiator particles that are encapsulated when the relative quantities of the reactive composition to the glass beads are varied. Additionally, Table 2 evaluates the effect of polymerization quenching through the addition of a weak acid. Example 9 is conducted without quenching and Example 10 includes acid quenching after polymerization. In each Example, polymerization occurs substantially similarly to Examples 1 to 8.

TABLE 2 Ratio of Glass Beads to Example 9 Example 10 Reactive Monomer (grams) (No Quenching) (Quenching)  0.5:1 79%  100% 0.75:1 71%  100%   1:1 63%  100%   2:1 49% 98.9%

As depicted in Table 2, Example 9 achieves encapsulation rates of between 49% and 79% depending on the relative quantity, by weight, between the reactive monomer composition and the glass beads. Example 10, which includes acid quenching but identical ratios, has encapsulation rates between 98.9% and 100%. As such, Example 10 demonstrates that improved encapsulation efficiency results when a polymerization quenching step is performed.

Example 11 is an additional matrix encapsulation made by coating glass beads with molten brittle polyethylene wax. By volume, the wax encapsulation consisted of about 75% glass beads and 25% polyethylene wax.

Examples of shell encapsulation are made on various initiator matrices. Shell layers are formed by dispersing the matrices in water at about 700 rpm and then forming a shell layer. In each shell encapsulation, about 0.5 g of DEMM is added dropwise to the medium containing the matrices for every 5 g of polymerization initiator. Polymerization is then allowed to occur by contacting exposed polymerization initiators on the surface of the initiator matrices for about 1 hour under continued mixing. The polymerization is then terminated with the addition of 0.02 g of trifluoroacetic acid. Shell encapsulated particles are then filtered and rinsed with deionized water.

Example 12 is a polymerizable system that includes encapsulated initiator particles and a polymerizable composition. Example 12 is produced from the components depicted in Table 3; its physical properties are depicted in Table 4. The encapsulated initiator particles included in Table 3 are formed by undergoing a two-phase synthesis consisting of a matrix encapsulation step similar to the process used in Examples 1 to 8 and a shell encapsulation step similar to the previously described shell encapsulation. The encapsulated initiator particles are then incorporated into a thickened methylene malonate formulation formed from the components described in Table 3. The encapsulated initiator particles of Example 12 also demonstrate the effect of using a blend of reactive monomers having different glass transition temperatures. The encapsulated initiator particles have a glass transition temperature of −21° C. which is between the glass transition temperatures of polymerized HMMM (−34° C.) and polymerized DEMM (35° C.).

TABLE 3 (Example 12) Encapsulated Initiator Particle Percent Glass Beads 47.50% DEMM    5% HMMM   45% Dimethyl Sebacate  2.50% Polymerizable System Percent Microcapsules   10% DEMM/DMMM Blend   66% HMMM   11% Polymeric Thickener   13% Stabilizers Trace

Table 4 depicts the physical properties of Example 12. As illustrated by Table 4, Example 12 exhibits excellent adhesive qualities.

TABLE 4 Property Measured Measurements Viscosity (Cone and Plate 3,000 to 5,000 cPs at 25° C., 15-20 rpm, and 40-70% torque) Accelerated Shelf Life Testing 12 days at 50° C. Color (Uncured/Cured) Transparent/Transparent Odor Sharp, sweet Set Time About 5-10 minutes on non-porous substrates Open Time 1 + hours (cure only begins after rupturing of the microcapsules) Cure Time About 4 hours

Table 5 depicts two additional examples of polymerizable systems: Examples 13 and 14. Each of Examples 13 and 14 additionally include trace quantities of MSA (10 ppm) and MeHQ (100 ppm) which act as stabilizers for the polymerizable composition.

TABLE 5 Components Example 13 Example 14 Dimethyl methylene malonate — 65.2% Diethyl methylene malonate 65.2% — Hexyl methyl methylene 12.3% 12.3% malonate Vinyl chloride terpolymer 10.5% 10.5% (thickener) Hydrophobic fumed silica  2.0%  2.0% (thixotropic agent) Micro-encapsulated glass beads 10.0% 10.0%

FIGS. 4 and 5 depict the tensile shear strength and cure profile of Examples 13 and 14. The tensile shear strength is measured on hard maple, steel, stainless steel, aluminum, acrylic, polycarbonate, ABS, and PVC.

Table 6 depicts the set time of Example 14 on various substrates.

TABLE 6 Lower Upper Substrate Limit (min) Limit (min) Hard Maple 45 60 Steel 2.75 7 Stainless Steel 4.75 9.5 Aluminum 4.5 9 Acrylic 4 8.75 Polycarbonate 4.5 7.5 ABS 4 7 PVC 3.5 6.5

The polymerizable compositions are also useful as threadlocking compositions. Table 7 depicts the performance properties of two threadlocking compositions: a comparative two-part system and a one-part system incorporating microencapsulated polymerization initiators. Comparative Example 15 is a two-part diethyl methylene malonate composition that cures, by the application of a secondary sodium benzoate initiator, in 30 seconds. Inventive Example 16 includes microencapsulated polymerization initiators and cures in about 5 minutes after the microencapsulated polymerization initiators are ruptured through mechanical shear. Strength and chemical resistance of each system were measured using Grade 2 steel bolts and nuts. Results of each Example are reported as the break-loose torque (Nm) required to break the bond.

TABLE 7 Comparative Inventive Break-Loose Torque (Nm) Example 15 Example 16 After 1 Hour 16 15 After 24 Hours 28 29 After exposure to 120° C. 16 24 After exposure to −20° C. 17.5 25 After exposure to gasoline 11.5 18.5 After exposure to acetone 14 23 After exposure to boiling 18 27 water

The dimensions and values disclosed herein are not to be understood as being strictly limited to the exact numerical values recited. Instead, unless otherwise specified, each such dimension is intended to mean both the recited value and a functionally equivalent range surrounding that value.

It should be understood that every maximum numerical limitation given throughout this specification includes every lower numerical limitation, as if such lower numerical limitations were expressly written herein. Every minimum numerical limitation given throughout this specification will include every higher numerical limitation, as if such higher numerical limitations were expressly written herein. Every numerical range given throughout this specification will include every narrower numerical range that falls within such broader numerical range, as if such narrower numerical ranges were all expressly written herein.

Every document cited herein, including any cross-referenced or related patent or application, is hereby incorporated herein by reference in its entirety unless expressly excluded or otherwise limited. The citation of any document is not an admission that it is prior art with respect to any invention disclosed or claimed herein or that it alone, or in any combination with any other reference or references, teaches, suggests, or discloses any such invention. Further, to the extent that any meaning or definition of a term in this document conflicts with any meaning or definition of the same term in a document incorporated by reference, the meaning or definition assigned to that term in the document shall govern.

The foregoing description of embodiments and examples has been presented for purposes of description. It is not intended to be exhaustive or limiting to the forms described. Numerous modifications are possible in light of the above teachings. Some of those modifications have been discussed and others will be understood by those skilled in the art. The embodiments were chosen and described for illustration of various embodiments. The scope is, of course, not limited to the examples or embodiments set forth herein, but can be employed in any number of applications and equivalent articles by those of ordinary skill in the art. Rather it is hereby intended the scope be defined by the claims appended hereto.

It should be understood that certain aspects, features, structures, or characteristics of the various embodiments can be interchanged in whole or in part. Reference to certain embodiments means that a particular aspect, feature, structure, or characteristic described in connection with certain embodiments can be included in at least one embodiment and may be interchanged with certain other embodiments. The appearances of the phrase “in certain embodiments” in various places in specification are not necessarily all referring to the same embodiment, nor are certain embodiments necessarily mutually exclusive of other certain embodiments. It should also be understood that the steps of the methods set forth herein are not necessarily required to be performed in the orders described, and the order of the steps of such methods should be understood to be merely exemplary. Likewise, additional steps can be included in such methods, and certain steps may be omitted or combined, in methods consistent with certain embodiments. 

What is claimed is:
 1. An encapsulated initiator particle comprising: an initiator matrix comprising: a first cured composition comprising one or more 1,1-disubstituted alkene compounds; and one or more polymerization initiators substantially encapsulated by the first cured composition and comprising spherical, non-spherical, irregular, angular, textured, or layered particles having an average granulometry of about 0.1 microns to about 1,000 microns.
 2. The encapsulated initiator particle of claim 1, wherein the one or more 1,1-disubstituted alkene compounds are selected from the group consisting of methylene malonates, methylene β-ketoesters, methylene β-diketones, dialkyl disubstituted vinyls, dihaloalkyl disubstituted vinyls, monofunctional, difunctional or multifunctional monomers, oligomers, or polymers thereof, and combinations thereof.
 3. The encapsulated initiator particle of claim 1, wherein the first cured composition comprises one or more low Tg 1,1-disubstituted alkene compounds.
 4. The encapsulated initiator particle of claim 1, wherein said polymerization initiators comprise one or more alkali metal salts, alkaline earth metal salts, ammonium salts, amine salts, halides, or metal oxides.
 5. An encapsulated initiator particle comprising: an initiator matrix comprising: a first cured composition comprising one or more 1,1-disubstituted alkene compounds; and one or more polymerization initiators substantially encapsulated by the first cured composition; and wherein the ratio of the first cured composition to said polymerization initiators is a ratio of about 1:1 to a ratio of about 2:1, by weight.
 6. The encapsulated initiator particle of claim 1 ruptures when about 0.1 psi or more of mechanical force is applied.
 7. The encapsulated initiator particle of claim 1, further comprising a shell layer, wherein the shell layer surrounds and encapsulates the initiator matrix.
 8. The encapsulated initiator particle of claim 7, wherein the shell layer is formed from one or more of a second cured composition formed of one or more 1,1-disubstituted alkene compounds; a urea formaldehyde resin; a polyvinyl alcohol; a gelatin; an acrylate; and a cured oligomeric reactive monomer.
 9. The encapsulated initiator particle of claim 8, wherein the 1,1-disubstituted alkene compounds of the second cured composition comprise one or more difunctional or multifunctional 1,1-disubstituted alkene compounds.
 10. The encapsulated initiator particle of claim 8, wherein the shell layer comprises the second cured composition and wherein the first cured composition and the second cured composition are different.
 11. The encapsulated initiator particle of claim 8, wherein the one or more 1,1-disubstituted alkene compounds of the second cured composition comprise an elevated temperature Tg 1,1-disubstituted alkene compound.
 12. The encapsulated initiator particle of claim 5, wherein the one or more 1,1-disubstituted alkene compounds are selected from the group consisting of methylene malonates, methylene β-ketoesters, methylene β-diketones, dialkyl disubstituted vinyls, dihaloalkyl disubstituted vinyls, monofunctional, difunctional or multifunctional monomers, oligomers, or polymers thereof, and combinations thereof.
 13. The encapsulated initiator particle of claim 5, wherein the first cured composition comprises one or more low Tg 1,1-disubstituted alkene compounds.
 14. The encapsulated initiator particle of claim 5, wherein said polymerization initiators comprise one or more alkali metal salts, alkaline earth metal salts, ammonium salts, amine salts, halides, or metal oxides.
 15. The encapsulated initiator particle of claim 5 ruptures when about 0.1 psi or more of mechanical force is applied.
 16. The encapsulated initiator particle of claim 5, further comprising a shell layer, wherein the shell layer surrounds and encapsulates the initiator matrix.
 17. The encapsulated initiator particle of claim 16, wherein the shell layer is formed from one or more of a second cured composition formed of one or more 1,1-disubstituted alkene compounds; a urea formaldehyde resin; a polyvinyl alcohol; a gelatin; an acrylate; and a cured oligomeric reactive monomer.
 18. The encapsulated initiator particle of claim 17, wherein the 1,1-disubstituted alkene compounds of the second cured composition comprise one or more difunctional or multifunctional 1,1-disubstituted alkene compounds.
 19. The encapsulated initiator particle of claim 17, wherein the shell layer comprises the second cured composition and wherein the first cured composition and the second cured composition are different.
 20. The encapsulated initiator particle of claim 17, wherein the one or more 1,1-disubstituted alkene compounds of the second cured composition comprise an elevated temperature Tg 1,1-disubstituted alkene compound. 